Understanding adhesion of gold conductive films on sodium alginate by photoelectron spectroscopy
Authors: Capelli R., Maccagnani P., Dinelli F., Murgia M., Bertoldo M., Montecchi M., Doyle B. P., Carleschi E., Pasquali L.
Autors Affiliation: 1 Dipartimento di Ingegneria E. Ferrari, Università di Modena e Reggio Emilia, Via Vivarelli 10,
41125 Modena, Italy
2 CNR – Istituto Officina dei Materiali, S.S. 14, km 163.5 in Area Science Park, 34012 Trieste, Italy
3 Department of Physics, University of Johannesburg, PO Box 524, Auckland Park, 2006, South
4 CNR – Istituto per la Microelettronica e Microsistemi, via P. Gobetti 101, 40129 Bologna, Italy
5 CNR – Istituto Nazionale di Ottica, via G. Moruzzi 1, 56124 Pisa, Italy
6 CNR – Istituto per lo Studio dei Materiali Nanostrutturati, via P. Gobetti 101, 40129 Bologna, Italy
7 CNR – Istituto per la Sintesi Organica e la Fotoreattività, via P. Gobetti 101, 40129 Bologna, Italy
Abstract: Ultrathin layers of gold, from 2 to 25 nm of nominal coverage, have been deposited on sodium-alginate biopolymer foils applying two alternative approaches: low power sputtering and thermal evaporation. The morphology of the deposited layers was obtained by means of atomic force microscopy. In the early stages of growth, thermal evaporation gives rise to a top surface resembling the underlying substrate, whereas low power sputtering produces a topography characterized by smoother areas. This indicates that the film growth occurs in different ways. X-ray photoelectron spectroscopy with two photon energies, corresponding to Al Kα and Ag Lα photons, was used to get information on the chemistry at the interface and on the degree of intermixing between Au and sodium-alginate. While no chemical modifications with respect to the bare materials could be detected, the evolution of the intensities of the relevant core levels of Au and sodium alginate (Au 4f and Na 1s in particular) indicated a strong intermixing in the case of films deposited by low power sputtering. This is further supported by optical measurements. The observed behaviour can be correlated with the enhanced adhesion of sputtered films compared to thermally evaporated ones.
Journal/Review: THIN SOLID FILMS
Volume: 690 Pages from: 137535 to: 137540
KeyWords: Sputtering deposition, Thermal evaporation, Gold thin films, Biopolymer, X-ray photoelectron spectroscopyDOI: 10.1016/j.tsf.2019.137535Citations: 3data from “WEB OF SCIENCE” (of Thomson Reuters) are update at: 2022-01-16References taken from IsiWeb of Knowledge: (subscribers only)Connecting to view paper tab on IsiWeb: Click hereConnecting to view citations from IsiWeb: Click here