Modification of wetting properties of laser-textured surfaces by depositing triboelectrically charged Teflon particles

Anno: 2013

Autori: Bayer I.S., Brandi F., Cingolani R., Athanassiou A.

Affiliazione autori: Center for Biomolecular Nanotechnologies at UNILE, Istituto Italiano di Tecnologia (IIT), Via Barsanti 1, 73010 Arnesano Lecce, Italy;
Department of Mechanical and Aerospace Engineering, University of Virginia, 122 Engineer’s Way, Charlottesville, VA 22904, United States;
Italian Institute of Technology (IIT), via Morego 30, 16152 Genoa, Italy

Abstract: Hydrophilic laser-textured silicon wafers with natural oxide surfaces were rendered hydrophobic by depositing electrostatically charged submicrometer Teflon particles, a process termed as triboelectric Teflon adhesion. Silicon surfaces were micro-textured (~5 µm) by laser ablation using a nanosecond pulsed UV laser. By varying laser fluence, micro-texture morphology of the wafers could be reproduced and well controlled. Wetting properties of the triboelectrically charged Teflon-deposited surfaces were studied by measuring apparent static water contact angles and water contact angle hysteresis as a function of substrate roughness and the amount of Teflon deposited. A similar study was also performed on various micro-textured silicon carbide surfaces (sandpapers). If the average substrate roughness is between 15 and 60 µm, superhydrophobic surfaces can be easily formed by Teflon deposition with water contact angle hysteresis less than 8. This environmentally benign solvent-free process is a highly efficient, rapid, and inexpensive way to render contact-charged rough surfaces hydrophobic or superhydrophobic.

Giornale/Rivista: COLLOID AND POLYMER SCIENCE

Volume: 291 (2)      Da Pagina: 367  A: 373

Parole chiavi: Laser ablation; Triboelectric polymer; Teflon; Textured surfaces; Superhydrophobicity
DOI: 10.1007/s00396-012-2757-0

Citazioni: 34
dati da “WEB OF SCIENCE” (of Thomson Reuters) aggiornati al: 2024-03-24
Riferimenti tratti da Isi Web of Knowledge: (solo abbonati)
Link per visualizzare la scheda su IsiWeb: Clicca qui
Link per visualizzare la citazioni su IsiWeb: Clicca qui